Enhancement of Current-Voltage Characteristics of Multilayer Organic Light Emitting Diodes by using Nanostructured Composite Films

Nguyen, Nang Dinh and Le, Ha Chi and Tran, Thi Chung Thuy and Tran, Quang Trung and Vo, Van Truong (2009) Enhancement of Current-Voltage Characteristics of Multilayer Organic Light Emitting Diodes by using Nanostructured Composite Films. Journal of Applied Physics, 105 (9). 093518-093518.

Full text not available from this repository.

Abstract

With the aim of improving the photonic efficiency of an organic light emitting diode (OLED) and its display duration, both the hole transport layer (HTL) and the emitting layer (EL) were prepared as nanostructured thin films. For the HTL, nanocomposite films were prepared by spin-coating a homogeneous solution of low molecular weight poly(4-styrenesulfonate) (PEDOT-PSS) and surfactant-capped TiO2 nanocrystals onto low resistivity indium tin oxide (ITO) substrates; for the EL, nancrystalline titatium oxide (nc-TiO2)-embedded Poly2-methoxy-5-(2′-ethyl-hexyloxy)-1,4-phenylene vinylene (MEH-PPV+nc-TiO2) conjugate polymers were spin-coated onto the HTL. Also, for a shallow contact of Al/LiF/MEH-PPV instead of Al/MEH-PPV a super LiF thin film was deposited onto the EL by vacuum evaporation. The resulting multilayer OLED had the following structure of Al/LiF/MEH-PPV+nc-TiO2/PEDOT-PSS+nc-TiO2/ITO. Characterization of the nanocomposite films showed that both the current-voltage (I-V) characteristics and the photoluminescent properties of the nanocomposite materials were significantly enhanced in comparison with the standard polymers. OLEDs made from these layers would exhibit a large photonic efficiency.

Item Type: Article
Uncontrolled Keywords: nanocomposites;organic light emitting diodes;organic semiconductors;photoluminescence;spin coating;thin films;titanium compounds;6146-w;7363-b;7867Bf;8107-b;8115-z;8560Jb
Subjects: ?? Nano ??
Divisions: Faculty of Engineering Physics and Nanotechnology (FEPN)
Depositing User: Prof. Xuan-Tu Tran
Date Deposited: 27 Mar 2013 06:31
Last Modified: 27 Mar 2013 06:31
URI: http://eprints.uet.vnu.edu.vn/eprints/id/eprint/145

Actions (login required)

View Item View Item